Mineral Reinforced Polypropylene Compound
Mineral-filled polypropylene compounds (BATOLEN) are a type of engineering thermoplastic produced by adding fillers such as talc and calcium carbonate to enhance mechanical and thermal properties. The improved strength and stiffness, better thermal resistance, dimensional stability, and competitive pricing are key features that make these compounds effective for manufacturing parts through the plastic injection process. Polypropylene compounds are widely used in the electronics, automotive, and household appliance industries. The knowledge-based company, Baspar Tose’e Davam Shimi, is capable of custom designing and producing various mineral-filled polypropylene compounds to meet the diverse needs of its customers, in addition to the existing grades.
Technical specifications
Mineral-filled reinforced polypropylene compounds are a type of engineering blend that not only possess good mechanical properties but are also widely used due to their lower cost compared to other grades. These compounds are extensively utilized in the automotive industry, packaging, household appliances, and electrical and electronic components. Bapar Tose’e Davam Chimi Company is capable of producing various types of polypropylene compounds reinforced with mineral fillers, with talc and calcium carbonate content ranging from 10% to 40%, tailored to the specific applications and needs of customers. The demand in engineering industries for components with high mechanical properties has driven us to continually strive to provide and produce high-quality reinforced polypropylene compounds with customizable options. Engineering polypropylene compounds are available in a variety of colors, including black, for sale in both domestic and international markets. The engineers at Baspar Tose’e Davam Shimi are always working to offer the most suitable grades of reinforced polypropylene compounds for the manufacturing of prefabricated and final parts through the plastic injection process to consumers and engineers in the production sector. It is worth mentioning that designing and producing customer-specific formulations, as well as consulting and providing the best processing conditions, are additional services offered by Baspar Tose’e Davam Chimi Company, carried out by the company's research and development team. Below are some of the properties of mineral-filled reinforced polypropylene compounds.
Variety of grades
| Specification | Unit | BATOPOL | ||||||
|---|---|---|---|---|---|---|---|---|
| CT20-NC | CT25-NC | HT20-NC | CT25-NC | HPW60 | HPC45N | |||
| Physical Properties | Type | Good quality 20% Talc reinforced | Good quality 25% Talc reinforced | Good quality 20% Talc reinforced | Good quality 25% Talc reinforced | Good quality high-filled reinforced | Good quality high-filled reinforced | |
| Density | g/cm3 | 1.05/td> | 1.08 | 1.05 | 1.08 | 1.36 | 1.99 | |
| Shrinkage | % | ≤0.2 | ≤0.2 | ≤0.2 | ≤0.2 | ≤0.2 | ≤0.9 | |
| Moisture absorption | % | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 | |
| Mechanical Properties | MFI | g/10min | 6-9 | 18 | 7-10 | 18 | 3 | |
| Tensile strength at break | MPa | 20-22 | 24-28 | 26-30 | 20 | 75 | ||
| Elongation at break | % | 8 | 6 | 9 | 7 | 5 | 9 | |
| Tensile modulus | MPa | 1850 | 1800 | 1900 | 1850 | 1700 | 1750 | |
| Izod impact, notched | kJ/m2 | 6-8 | 4-5 | 5-8 | 5-7 | 4 | 14 | |
| Hardness | 75 | 75 | 75 | 75 | 75 | 75 | ||
| Temporal Properties | Melting temperature (10K/min) | ͦC | 160 | 160 | 160 | 160 | 165 | 165 |
| Heat deformation temperature (0.45 MPa) | ͦC | 90 | 90 | 90 | 90 | 155 | 155 | |
| Heat deformation temperature (1.8 MPa | ͦC | 80 | 80 | 80 | 80 | 150 | 150 | |
Process parameters
Applications
Automobile Industry
Electricity and Electronics
Home Appliances Industry